{"id":30229,"date":"2021-06-22T06:26:52","date_gmt":"2021-06-22T06:26:52","guid":{"rendered":"http:\/\/sitepourvtc.com\/?page_id=30229"},"modified":"2023-09-14T13:03:03","modified_gmt":"2023-09-14T13:03:03","slug":"martensite","status":"publish","type":"page","link":"https:\/\/sitepourvtc.com\/nuclear-engineering\/materials-science\/phase-diagrams-of-iron-carbon-system\/martensite\/","title":{"rendered":"Martensite – Martensitic Steel"},"content":{"rendered":"
\n

\"Martensite\"<\/a>Martensite<\/strong> is a very hard metastable structure with a body-centered tetragonal (BCT) crystal structure. Martensite is formed in steels when austenite’s cooling rate is so high that carbon atoms do not have time to diffuse out of the crystal structure in large enough quantities to form cementite (Fe3<\/sub>C). Therefore, it is a product of diffusionless transformation, and any<\/strong>\u00a0diffusion whatsoever results in the formation of ferrite and cementite phases. It is named after the German metallurgist Adolf Martens<\/strong> (1850\u20131914).<\/p>\n

Unlike the isothermal decomposition of phase constituents by diffusion, martensite is not a phase associated with thermal equilibrium. Thus, it does not appear on the iron-carbon equilibrium phase diagram. It may be thought of as a transformation product that is competitive with pearlite and bainite.<\/p>\n

The microstructure of martensite in steels has different morphologies and may appear as either lath martensite or plate martensite. For steel 0\u20130.6% carbon, the martensite has the appearance of lath and is called lath martensite<\/strong>. For steel greater than 1% carbon, it will form a plate-like structure called plate martensite<\/strong>. Plate martensite, as the name indicates, forms lenticular (lens-shaped) crystals with a zigzag pattern of smaller plates. Between those two percentages, the physical appearance of the grains is a mix of the two. The strength of the martensite is reduced as the amount of retained austenite grows.<\/p>\n

Martensitic Transformation<\/h2>\n

Transformation hardening, also known as martensitic transformation hardening, is one of the most common hardening methods primarily used for steels (i.e., carbon steels and stainless steels). The martensitic transformation is not unique to iron-carbon a and its, and it is found in other systems and is characterized, in part, by diffusionless transformation.<\/p>\n

Martensitic steels<\/strong> use predominantly higher levels of C and Mn and heat treatment to increase strength. The finished product will have a duplex ferrite microstructure with varying levels of degenerate marte, allowing for varying levels of strength. In metallurgy, quenching is commonly used to harden steel by introducing martensite. There is a balance between hardness and toughness in any steel; the harder the steel, the less tough or impact-resistant it is, and the more impact-resistant it is, the less hard it is.<\/p>\n

Martensite is produced from austenite due to quenching or another form of rapid cooling. Austenite in iron-carbon alloys is generally only present above the critical eutectoid temperature (723\u00b0C) and below 1500\u00b0C, depending on carbon content. In the case of normal cooling rates, as the austenite cools, the carbon diffuses out of the austenite, forms carbon-rich iron-carbide (cementite), and leaves behind carbon-poor ferrite. Depending on alloy composition, a layering of ferrite and cementite, called pearlite, may form. But in case of rapid cooling, the carbon does not have time enough to diffuse and then transforms into a highly strained body-centered tetragonal form called martensite that is supersaturated with carbon. All the carbon atoms remain interstitial impurities in martensite. The cooling rate determines the relative proportions of martensite, ferrite, and cementite. It, therefore, determines the mechanical properties of the resulting steel, such as hardness, tensile strength, and toughness.<\/p>\n

Tempered Martensite<\/h2>\n

The relative ability of a ferrous alloy to form martensite is called hardenability. Hardenability is commonly measured as the distance below a quenched surface at which the metal exhibits a specific hardness of 50 HRC, for example, or a specific percentage of martensite in the microstructure. The highest hardness of pearlitic steel is 43 HRC, whereas martensite can achieve 72 HRC. Fresh martensite<\/strong> is very brittle if the carbon content is greater than approximately 0.2 to 0.3%. It is so brittle that it cannot be used for most applications. This brittleness can be removed (with some loss of hardness) if the quenched steel is heated slightly in a process known as tempering. Tempering is accomplished by heating martensitic steel to a temperature below the eutectoid for a specified period (for example, between 250\u00b0C and 650\u00b0C ).<\/p>\n

This tempering heat treatment allows, by diffusional processes, the formation of tempered martensite, according to the reaction:<\/p>\n

martensite (BCT, single phase) \u2192 tempered martensite (ferrite + Fe3<\/sub>C phases)<\/p>\n

The single-phase BCT martensite, supersaturated with carbon, transforms into the tempered martensite<\/strong>, composed of the stable ferrite and cementite phases. Its microstructure is similar to the microstructure of spheroidite, but in this case, tempered martensite contains extremely small and uniformly dispersed cementite particles embedded within a continuous ferrite matrix. Tempered martensite may be nearly as hard and strong as martensite but with substantially enhanced ductility and toughness.<\/p>\n

Martensitic Stainless Steel<\/h2>\n

\"MartensiticMartensitic stainless steels<\/a><\/strong> are similar to ferritic steels based on chromium but have higher carbon levels<\/strong> up, as high as 1%. They are sometimes classified as low-carbon and high-carbon martensitic stainless steels. They contain 12 to 14% chromium, 0.2 to 1% molybdenum, and no significant amount of nickel. Higher amounts of carbon allow them to be hardened and tempered, much like carbon and low-alloy steels. They have moderate corrosion resistance<\/strong>\u00a0but are considered hard, strong, and slightly brittle<\/strong>. They are magnetic and <\/strong>can be nondestructively tested using the magnetic particle inspection method, unlike austenitic stainless steel. A common martensitic stainless is AISI 440C, which contains 16 to 18% chromium and 0.95 to 1.2% carbon. Grade 440C stainless steel is used in the following applications: gage blocks, cutlery, ball bearings and races, molds and dies, and knives.<\/p>\n

As was written, martensitic stainless steels can be hardened and tempered through multiple ways of aging\/heat treatment<\/strong>: The metallurgical mechanisms responsible for the martensitic transformations that take place in these stainless alloys during austenitizing and quenching are essentially the same as those that are used to harden lower-alloy-content carbon and alloy steels. The heat treatment typically involves three steps:<\/p>\n